| SUBJECT |
THICKNESS |
REMARKS |
| 15 mm |
25 mm |
45 mm |
Specific Density (kg/m3) |
< 500 |
ASTM D1037-99 Modified |
Compressive Strength (kg/cm2) |
9 |
10 |
10 |
ASTM D1037-99 Modified |
| Max. Load of Static Bending (kgf) |
15 |
41 |
62 |
ASTM D1037-99 Modified |
| Falling Ball Impact Test (mm) |
925 |
900 |
1275 |
ASTM D1037-99 Modified
(Impact Resistance) |
| Thermal Conductivity (W/m.K) |
0.09 |
0.08 |
0.08 |
ASTM C518-04 |
| Thermal Resistance (m2.K/W) |
0.29 |
0.41 |
0.56 |
ASTM C518-04 |
| Fire Resistance |
2 Hours |
CNS 12514/A3305 (no toxic gas released) |
| Incombustibility |
2nd Grade |
CNS 6532 (2003) |
| Sound Absorption |
NRC = 0.65 |
ASTM C423 |
| Acid Resistance |
No chap, No color changed |
Immersed in 5% Acetic acid after 24 hours |
| Chemical Resistance |
No Damage |
ASTM D543-06, 5%NaOH,
5%KoH, 5%Na2CO3 |
| Mold Resistance |
Yes |
ASTM G-21-96 |
| TVOC (mg/m2.hr) |
0.106 |
ASTM D5116-97 (< 0.19 mg/m2.hr) |
| Formaldehyde HCHO (mg/m2.hr) |
No |
ASTM D5116-97 (< 0.08 mg/m2.hr) |
| Percentage change of Dimension (%) |
Longitudinal:0.29 |
ASTM D570-98
Immersion in water for 23°C , 72 hrs |
| Transverse:0.09 |